DongGuan UsenStar Plastic Raw Material CO, . Ltd
Home > Products > Scrap Rubber & Recycled Rubber > PC Plastic Raw Maaterial

PC Plastic Raw Maaterial

— ET3113 550115, PC RESIN, BAYER
Product Category: Scrap Rubber & Recycled Rubber
Sales Method: Export, Manufacture, Service, Retail
Payment Term: T/T
Min. Order Unit Price
Contact Info

Mr.Robert

Address: China (mainland) Guangdong Dongguan,NO. 843 Suda RD, DaJingJiu Plastic Market ChangPing Town GD. China

Product Detail

Product Attribute:

  • Thailand More >
  • ET3113 550115 PC
  • BAYER
  • 08/22/2013
  • 08/23/2013

Additional Info.:

  • BAG

Product Content Description:

Formerly Makrolon 3103 MAS157; MVR (300 °C/1.2 kg) 6.0 cm³/10 min; Extrusion; High viscosity; UV stabilized; Available in transparent colors only; Solid sheet;

C Melt volume-flow rate 300 °C; 1.2 kg cm³/10 min ISO 1133 6.0
C Molding shrinkage, parallel 60x60x2 mm; 500 bar % ISO 294-4 0.7
C Molding shrinkage, normal 60x60x2 mm; 500 bar % ISO 294-4 0.75
Molding shrinkage, parallel/normal Value range based on general practical experience % b.o. ISO 2577 0.6 - 0.8
Melt mass-flow rate 300 °C; 1.2 kg g/10 min ISO 1133 6.5
Mechanical properties (23 °C/50 % r. h.)
C Tensile modulus 1 mm/min MPa ISO 527-1,-2 2350
C Yield stress 50 mm/min MPa ISO 527-1,-2 65
C Yield strain 50 mm/min % ISO 527-1,-2 6.3
C Nominal strain at break 50 mm/min % ISO 527-1,-2 > 50
Stress at break 50 mm/min MPa ISO 527-1,-2 70
Strain at break 50 mm/min % b.o. ISO 527-1,-2 130
C Tensile creep modulus 1 h MPa ISO 899-1 2200
C Tensile creep modulus 1000 h MPa ISO 899-1 1900
Flexural modulus 2 mm/min MPa ISO 178 2350
Flexural strength 2 mm/min MPa ISO 178 96
Flexural strain at flexural strength 2 mm/min % ISO 178 7.2
Flexural stress at 3.5 % strain 2 mm/min MPa ISO 178 72
C Charpy impact strength 23 °C kJ/m² ISO 179-1eU N
C Charpy impact strength -30 °C kJ/m² ISO 179-1eU N
Charpy impact strength -60 °C kJ/m² ISO 179-1eU N
Charpy notched impact strength 23 °C; 3 mm kJ/m² ISO 7391/b.o. ISO 179-1eA
80P
Charpy notched impact strength -30 °C; 3 mm kJ/m² ISO 7391/b.o. ISO
179-1eA
18C(P)
Izod notched impact strength 23 °C; 3.2 mm kJ/m² b.o. ISO 180-A 90P
Izod notched impact strength -30 °C; 3.2 mm kJ/m² b.o. ISO 180-A 16C(P)
C Puncture maximum force 23 °C N ISO 6603-2 5600
C Puncture maximum force -30 °C N ISO 6603-2 6500
C Puncture energy 23 °C J ISO 6603-2 60
C Puncture energy -30 °C J ISO 6603-2 70
Ball indentation hardness N/mm² ISO 2039-1 113

Send your inquiry to this supplier

- Your message must be between 20-3000 characters.

Browse

- jpg, jpeg, gif, txt, doc, pdf, xls, docx,xlsx, rar or zip format;
- Max. size of 2MB

Related Category Searches on ttnet.net: