Phos-Copper-Silver Brazing Rod BCuP-6/Silver 2%/Ag 2%

— Copper-Silver, TC209, 2% Silver Solding
Product Category: Copper Coils & Strips
Sales Method: Manufacture, OEM/ODM
Payment Term: T/T
Trade Term (Incoterms): FOB, CIF, CIP
Min. Order Unit Price
1 Piece
Contact Info

Ms.Jane

Address: China (mainland) Shanghai Shanghai,B302, No. 1065 West Zhongshan Road Changning District, Shanghai, China

Product Detail

Product Attribute:

  • China (mainland) More >
  • 08/29/2017
  • 08/29/2017

Product Content Description:

Sanhuan SAgP-2
Chemical Composition %
Silver 1.8-2.2
Copper Rem
Phosphorus 6.8-7.2
Other Elements 0.15Max
Physical Properties
Solidus 1190ºF(643 ºC)
Liquidus 1450ºF(788 ºC)
Brazing Temperature 1350ºF-1500ºF(732ºC-816 ºC)
Specific Gravity 8.01
Density(lbs/in3) 0.29
Specifications    
AWS A5.8/A5.8M BCuP-6
ASME SECTION II, PART C SFA-5.8 BCuP-6
Brazing Characteristics
Sanhuan Low-Silver/Phos-Copper-Silver brazing alloy SAgP-2 is a copper rich, intermediate temperature, brazing filler metal which has good mobility and processing property. The phosphorous content form its "self-fluxing" properties when used on copper. However, when joint copper base alloys, such as brass or bronze, braze with flux SFB-102 is recommended. The level of phosphorous also changes the fluidity and ductility of the material. The greater the percentage of phosphorous in the filler metal the more fluid the material will be. Phos-Copper filler metal should not be used on ferrous or nickel-based alloys or on copper-nickel alloys containing a nickel content in excess of 10%, as brittle intermetallic compounds are formed at the filler metal-base metal interface. Corrosion resistance is comparable to that of copper except when exposed to sulfurous containing compounds, especially at elevated temperatures.
Application
Sanhuan Phos-Copper-Sliver brazing alloy SAgP-2 is a economical, low silver alloy, it designed to broaden the melting range of Sanhuan SCuP-2. It has the ability to fill wide joints clearance at the lower end of its brazing range. At the high end of the brazing range, it is more fluid. Joint clearance of 0.002in. to 0.005in. [0.05mm to 0.13mm] are recommended.
 
Available Forms
Rods, Wires, Flats, Rings, Coils 
 
The Technical Services Department at Harhigh is available to help answer any questions you may have with regard to your specific brazing application, joint design and filler metal selection. 

Send your inquiry to this supplier

- Your message must be between 20-3000 characters.

Browse

- jpg, jpeg, gif, txt, doc, pdf, xls, docx,xlsx, rar or zip format;
- Max. size of 2MB

Related Category Searches on ttnet.net:

Related Keyword Seraches on ttnet.net: